3D Print investment materials
Phosphate-bonded precision investment for pressable ceramics in rapid prototyping
For printed and milled wax and resin frameworks, rapid heating
For small bridges, crowns, and inlays
Exact fit
Easy devesting with low blasting pressure
No investment-related layer on pressed objects
Mixing ratio24 ml liquid : 100 g powder
Setting time30 min
Final temperature850 °C
Total expansion3.1% (100% conc.)
6kg (30 x 200g bags) (REF CC0200)
1000 ml liquid (REF CC0210)
5000 ml liquid (REF CC0220)
Phosphate-bonded precision investment for model casting using rapid prototyping
For printed and milled wax and resin frameworks, rapid heating
Thin-flowing and long working time
Models smooth and edge-stable
Exceptional fits
Classic, step-by-step preheating also possible
Mixing ratio20 ml liquid : 100 g Powder
Recommended final temperature850 - 900 °C
6kg (30 x 200g bags) (REF CC0300)
1000 ml liquid (REF CC0310)
5000 ml liquid (REF CC0320)
Phosphate-bonded precision investment for crowns and bridges using rapid prototyping
For printed and milled wax and resin frameworks, rapid heating
Excellent flow properties and long working time
Very soft when deflasking
High Expansion Liquid available
Classic, step-by-step preheating also possible
Mixing ratio28 ml liquid : 100 g Powder
Setting time30 min (22 °C)
PreheatingSpeed | Gradually with holding times
Final temperature650 - 900 °C
Total expansion3.1% (100% conc.)
6 kg (30 x 200 g bags) (REF CC0400)
1000 ml Liquid (REF CC0410)
5000 ml Liquid (REF CC0420)