Phosphate-bonded crown and bridge investment material for rapid heating
For non-precious and precious metal alloys and for rapid heating.
Excellent flow properties and long processing time
Very soft when devesting
High Expansion Liquid available
Ideal for telescopic work
Classic, step-by-step preheating also possible
Mixing ratio28 ml liquid : 100 g Powder
Setting time30 min (22 °C)
PreheatingSpeed | Gradually with holding times
Final temperature650 - 900 °C
Total expansion3.1% (100% conc.)
4.5 kg (30 x 150 g bags) (REF 3060)
500 ml liquid (REF 3065)
1000 ml liquid (REF 3066)
5000 ml liquid (REF 3067)
1000 ml High Expansion Liquid (REF 3069)
Phosphate-bonded crown and bridge investment material for rapid heating
For non-precious and precious metal alloys and for rapid heating.
Only 20 minutes setting time
Casting result after approx. 60 minutes
Special liquid available for higher expansions
Classic, gradual preheating also possible
Mixing ratio22 ml liquid : 100 g powder
Setting time20 min (22 °C)
PreheatingSpeed | Step by step with holding times
Final temperature650 - 900 °C
Total expansion3.3% (100% conc.)
4.5 kg (30 x 150 g bags) (REF 3050)
1000 ml liquid (REF 3055)
5000 ml liquid (REF 3058)
1000 ml special liquid (REF 3056)
5000 ml special liquid (REF 3059)
Phosphate-bonded crown and bridge investment material for rapid heating
For non-precious and precious metal alloys and for rapid heating.
the classic from Feguramed
silky smooth, flawless casting surfaces
very soft when devesting
classic, gradual preheating also possible
Mixing ratio24 ml liquid: 100 g powder
Setting time30 min (22 °C)
PreheatingSpeed | Step by step with holding times
Final temperature650 - 900 °C
Total expansion2.9% (100% conc.)
6.0 kg (40 x 150 g bags) (REF 3025)
1000 ml special liquid (REF 3045)
5000 ml special liquid (REF 3046)
Phosphate-bonded crown and bridge investment material
For non-precious and precious metal alloys as well as for classic, gradual preheating.
the classic from Feguramed
silky smooth, flawless casting surfaces
special liquid available for higher expansions
very soft when devesting
Mixing ratio24 ml liquid : 100 g powder
Setting time30 min (22 °C)
PreheatingStep by step with holding times
Final temperature650 - 900 °C
Total expansion2.3 % (100 % conc.)
5 kg loose (REF 3013)
10 kg loose (REF 3014)
18 kg loose (REF 3015)
3 kg (20 x 150 g bag) (REF 3017)
6 kg (40 x 150 g bags) (REF 3018)
250 ml liquid (REF 3030)
1000 ml liquid (REF 3035)
5000 ml liquid (REF 3039)
250 ml special liquid (REF 3040)
1000 ml special liquid (REF 3043)
5000 ml special liquid (REF 3044)
Phosphate-bonded crown and bridge investment material for rapid heating
For non-precious and precious metal alloys and for rapid heating.
inexpensive alternative for solid casting results
highly thermally resilient
classic, gradual preheating also possible
Mixing ratio22 ml liquid : 100 g Powder
Setting time30 min (22 °C)
PreheatingSpeed | Step by step with holding times
Final temperature650 - 900 °C
Total expansion3.3% (100% conc.)
4.5 kg (30 x 150 g bags) (REF 3117)
1000 ml special liquid (REF 3126)
5000 ml special liquid (REF 3127)
Phosphate-bonded crown and bridge investment material
For non-precious and precious metal alloys as well as for classic, gradual preheating.
inexpensive alternative for solid casting results
highly thermally resilient
Mixing ratio22 ml liquid : 100 g powder
Setting time30 min (22 °C)
PreheatingStep by step with holding times
Final temperature650 - 900 °C
Total expansion2.2 % (100 % conc.)
4.5 kg (30 x 150 g bags) (REF 3110)
5 kg loose (REF 3114)
10 kg loose (REF 3115)
18 kg loose (REF 3116)
1000 ml liquid (REF 3124)
5000 ml liquid (REF 3125)